Aluminate hydration products have poor chemical stability due to phase transitions. From the electron micrographs of PACs, it can be seen that many acicular, flaky, and rod-like hydration products overlap and cross each other, and the aluminophosphates Hydration products have good chemical stability and show good early strength. After being calcined for 6 hours by 700e, it can be found from the electron microscope photos that PAC still contains a small amount of hydration products and gels. Due to the dehydration of the hydration products, more porous holes appear in the samples, and the sintered ceramic crystals are incompletely developed, resulting in a relatively normal temperature. Hydration significantly decreased by 1 day. Similar to HAC and PCA, its intensity also declined to varying degrees. After calcining at 1500e (HAC at 1400e), the SEM morphology clearly shows that the ceramic crystals formed after dehydration of the three kinds of cement crystals have grown, and the crystals in PCA and HAC are not only coarse, And the edge is relatively clear, the texture of the sample is dense, but there are some holes in the PCA. PAC can be developed into a new type of hydraulic, amorphous, refractory cement for amorphous refractory with good high temperature resistance. The main ore phases in PAC are: CA2, L, CxP, not only have high strength at normal temperature, but also have good fire resistance. In this study, PAC can be normal hydration and hardening with no need of adding any auxiliary admixture, and it can work well. At 1500e, PAC can still hold a higher compressive strength of 60.7MPa. The whole of the furnace is made of fire-resistant cement. Although it is relatively simple, it has a high cost, and the inner wall of the furnace is easy to collapse and is not easy to repair. In the process of alternating hot and cold, it is easy to crack and seep. After the furnace is fired with refractory bricks, it is built around refractory cement and has a long life, but the effect is not obvious. Tinted Glass is produced by the float process with the addition of small quantities of metal oxides to color the normal clear glass mix. This coloration is achieved through adding metal oxides at the smelting stage. Addition of color does not affect the basic properties of the glass, even though visible light reflectance will be slightly higher than clear glass. Patterned Glass, also known as figured glass is a kind of decorative translucent flat glass with embossed patterns on one or both surfaces. With the special property of decoration, patterned glass can fully allow the light to pass though and on the other hand can limit or prevent clear view effectively. It is mainly used on windows, indoor compartment, bathroom,etc. Stained Glass Panels,Patterned Glass For Doors,Patterned Mirror Glass,Tinted Patterned Glass Jinan Coton Glass Co., Ltd , https://www.cotonglass.com